AGESIN® Polyester modified polysiloxane copolymer solution
Product Number: AgeSin® LA-D510N
Equivalent alternatives: BYK-310, Elementis Levaslip 872
| Composition | Polyester modified polysiloxane copolymer solution |
| Appearance | Transparent to slight yellowish liquid |
| Solvent | Xylene |
| Density | 0.88-0.92 g/ml (25±1)℃ |
| Viscosity | 5-25s(Tu-4 viscometer)(25±0.2)℃ |
| Solid content | 25±3% (105℃ 3h) |
This data sheet is intended to give typical results, not standard.Subject to COA.
● Solvent-based/ UV Cure
● Reduce the coefficient of friction on the surface of the paint film, increase slip performance, improve scratch resistance, and increase gloss.
● Suitable for high-temperature baking paint system, good recoatability, does not affect the adhesion between layers.
● Used together with AgeSin® FS-D9013R, it can effectively prevent shrinkage and reduce dynamic surface tension (increase spray leveling speed and anti-orange peel ability).
● It will precipitate at low temperature, and become transparent after heating or diluted with solvent, which will not affect the product quality.
Can be added at any stage of the production process, including post-addition.
Suggest addition:
Addition to total formulation 0.1-0.5%
Transparency in varnish : 4
Defoaming : 2
Dynamic surface tension : 3
Static surface tension : 3
Slippery : 4
Anti-orange peel ability : 2
0=unavailable 5=very effective
● 25KG / 180KG
Being kept in dry, clean warehouse with well ventilation.
Avoid exposing to light and heating.
Protecting the product from leakage, rain and insolation during transportation.
Мы предлагаем широкий выбор вариантов, чтобы помочь вам найти подходящий продукт для ваших задач.
Оказание поддержки в оптимизации рецептур для систем на водной/растворительной основе.
Полное соответствие стандартам REACH, FDA и GB.
99,8% показатель своевременной доставки, гарантированная производственная мощность 10 000 тонн.